PA66(尼龍66)AKV30H3.0/德國朗盛/物性表參數

日期：2020-04-25 03:02:43 編輯：科思德塑膠來源：科思德塑膠瀏覽：307

德國朗盛 Durethan PA66 AKV30H3.0是一種加30%玻璃纖維p66, 注塑成型，熱老化穩定，表麵光潔度提高尼龍樹脂,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA66 AKV30H3.0

生產商：LANXESS(德國 朗盛)、品名：Durethan
PA66(尼龍66)AKV30H3.0/德國朗盛/物性表參數

C	These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
C	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.4
C	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	1.1
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.04
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	9500	6000
C	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	185	115
C	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.5	6.5
C	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	75	90
C	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	60	60
C	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	10	15
C	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	10	10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	65	70
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	55	55
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	10	15
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	9200	5500
	Flexural strength	2 mm/min	MPa	ISO 178-A	280	185
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.2	6.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	260	145
C	Puncture maximum force	23 °C	N	ISO 6603-2	1000	1100
C	Puncture maximum force	-30 °C	N	ISO 6603-2	800
C	Puncture energy	23 °C	J	ISO 6603-2	2.5	4.2
C	Puncture energy	-30 °C	J	ISO 6603-2	1.9
	Ball indentation hardness		N/mm²	ISO 2039-1	230	130
Thermal properties
C	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	262
C	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	240
C	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	>250
C	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	185
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 230
C	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.3
C	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
C	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
C	Burning behavior UL 94	0.75 mm	Class	UL 94	HB
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	700
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	700
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	700
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	725
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	725
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	725
	Burning behavior US-FMVSS302			ISO 3795	passed
C	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	> 230
Electrical properties (23 °C/50 % r. h.)
C	Relative permittivity	100 Hz	-	IEC 60250	4.5	9.0
C	Relative permittivity	1 MHz	-	IEC 60250	4.0	4.5
C	Dissipation factor	100 Hz	10-4	IEC 60250	250	1470
C	Dissipation factor	1 MHz	10-4	IEC 60250	240	730
C	Volume resistivity		Ohm·m	IEC 60093	1E13	1E10
C	Surface resistivity		Ohm	IEC 60093	1E15	1E14
C	Electric strength	1 mm	kV/mm	IEC 60243-1	40	39
C	Comparative tracking index CTI	Solution A	Rating	IEC 60112	525
Other properties (23 °C)
C	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	5.5
C	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.9
C	Density		kg/m³	ISO 1183	1360
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
C	Injection molding-Melt temperature		°C	ISO 294	290
C	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

德國朗盛 Durethan PA66 AKV30H3.0具有高抗震及抗裂性能，具體指標與材料的等級與含水量有關。彈性體改性的材料即使在低含水量及低溫下也具有良好的韌性,硬度高，尤其對於玻纖增強級別產品；拉伸模量：1,300 到 15,700 MPa (取決於含水量),良好的機械性能及阻尼吸聲效應、低摩擦力、急速運行能力好，氣體阻隔性能好（薄膜級）,

密度	1.01~1.23	模具溫度	80.0 到 100°C
加工（熔體）溫度	260 到 270°C	注射壓力	230 到 250°C
預熱	溫度/°C	130°C	工藝參數	注射時間	20~90
時間/h	4.0hr	高壓時間	0~5
料桶溫度/°C	後段	193 到 238°C	冷卻時間	20~90
中段	210 到 249°C	總周期	220 到 260°C
前段	221 到 254°C	螺杆轉數	30 到 60rpm
噴嘴溫度	232 到 274°C	使用注射機類型	螺杆式

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.

上一頁：PA66(尼龍66)AKV30H2.0/德國朗盛/物性表參數下一頁：PA66(尼龍66)AKV30HRH2.0/德國朗盛/物性表參數