德國朗盛 Durethan PA66 AM440H3.0是一種加30%玻璃纖維/礦物，注塑成型，熱老化穩定，不易變形尼龍樹脂,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
生產商：LANXESS(德國朗盛)、品名：Durethan
PA66(尼龍66)AM440H3.0/德國朗盛/物性表參數

C	These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
C	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	1.3
C	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	1.1
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.4
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.4
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	6100	2700
C	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	85	38
C	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.5	10
C	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	40	65
C	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	45	35
C	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	<10
C	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	35	45
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	35	35
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	5800	2700
	Flexural strength	2 mm/min	MPa	ISO 178-A	140	70
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.5	7.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	140	60
C	Puncture maximum force	23 °C	N	ISO 6603-2	610	640
C	Puncture maximum force	-30 °C	N	ISO 6603-2	610	610
C	Puncture energy	23 °C	J	ISO 6603-2	2.2	2.9
C	Puncture energy	-30 °C	J	ISO 6603-2	2.2	2
Thermal properties
C	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	265
C	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	110
C	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	230
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	245
C	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.6
C	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.8
Electrical properties (23 °C/50 % r. h.)
C	Comparative tracking index CTI	Solution A	Rating	IEC 60112	625
Other properties (23 °C)
C	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	4.5
C	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.7
C	Density		kg/m³	ISO 1183	1490
Processing conditions for test specimens
C	Injection molding-Melt temperature		°C	ISO 294	290
C	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.

上一頁：PA66(尼龍66)AM430H2.0/德國朗盛/物性表參數下一頁：PA6(尼龍6)B24CMH2.0/德國朗盛/物性表參數

返回首頁返回物性參數列表

PA66(尼龍66)AM440H3.0/德國朗盛/物性表參數

熱門文章

推薦文章