PA6(尼龍6)BKV30FN04/德國朗盛/物性表參數

日期：2020-04-14 09:47:19 編輯：科思德塑膠來源：科思德塑膠瀏覽：1106

德國朗盛 LANXESS Durethan PA6 BKV30FN04是一種加入30%玻璃纖維，注塑，無鹵阻燃，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA6 BKV30FN04

以下是PA6(尼龍6)BKV30FN04/德國朗盛/物性表參數

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.2
	Molding shrinkage, transverse	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.7
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	10300	6700
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	130	90
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3	6
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	60	68
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	55	50
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	13
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	55	65
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	13
	Flexural modulus	2 mm/min	MPa	ISO 178-A	10200	6600
	Flexural strength	2 mm/min	MPa	ISO 178-A	230	158
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.1	5.2
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A		140
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	220
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	205
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	219
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	212
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.8
	Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94	0.75 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V	1.5 mm	Class	UL 94	5VA
	Oxygen index	Method A	%	ISO 4589-2	32
	Glow wire test (GWFI)	0.4 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.4 mm	°C	IEC 60695-2-13	775
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	775
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	775
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	800
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.5
	Relative permittivity	1 MHz	-	IEC 60250	3.9
	Dissipation factor	100 Hz	10-4	IEC 60250	260
	Dissipation factor	1 MHz	10-4	IEC 60250	160
	Volume resistivity		Ohm·m	IEC 60093	7.3E+13
	Electric strength	1 mm	kV/mm	IEC 60243-1	30
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	4.6
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.5
	Density		kg/m³	ISO 1183	1423
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	260
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Melt temperature (Tmin - Tmax)		°C	-	250-280
	Mold temperature		°C	-	70-90