PA6(尼龍6)BKV30H2.0XF/德國朗盛/物性表參數

日期：2020-04-14 09:52:27 編輯：科思德塑膠來源：科思德塑膠瀏覽：259

德國朗盛 LANXESS Durethan PA6 BKV30H2.0XF是一種加入30%玻璃纖維，注塑，改善流動性，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA6 BKV30H2.0XF

以下是PA6(尼龍6)BKV30H2.0XF/德國朗盛/物性表參數

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.25
	Molding shrinkage, transverse	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.70
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.05
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.10
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	9000	5600
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	155	95
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3	5
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	75	80
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	50	45
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	10	15
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	65	70
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	50	50
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	10	20
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	8200	5400
	Flexural strength	2 mm/min	MPa	ISO 178-A	230	150
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.8	5
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	220	130
	Puncture maximum force	23 °C	N	ISO 6603-2	720	1000
	Puncture maximum force	-30 °C	N	ISO 6603-2	650	650
	Puncture energy	23 °C	J	ISO 6603-2	2.5	5.5
	Puncture energy	-30 °C	J	ISO 6603-2	2	2
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	221
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	215
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	1
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	7
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	2.1
	Density		kg/m³	ISO 1183	1350
	Bulk density		kg/m³	ISO 60	650
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	260
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	250-280
	Mold temperature		°C	-	80-120

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.

上一頁：PA6(尼龍6)BKV30H2.0LT/德國朗盛/物性表參數下一頁：PC(聚碳酸酯)PC-681U/奇美實業/物性表參數

返回首頁返回物性參數列表

PA6(尼龍6)BKV30H2.0XF/德國朗盛/物性表參數

熱門文章

推薦文章