VALOX(沙伯基礎)4012G/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX 4012G PBT是一種加10%玻璃纖維增強PBT注塑樹脂，具有優異的機械性能,應用程序:連接器,該等級為4012，具有更好的循環時間和延展性。
 |
沙伯基礎創新塑料的VALOX 4012G PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)4012G/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 80 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 80 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 4400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 80 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 80 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4500 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 125 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 120 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 5 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3800 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 110 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 33 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 33 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 380 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 380 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 4 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 6 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 6 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 205 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 4.63E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 8.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 6.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 4.79E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 2.11E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 205 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 170 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 185 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.35 | - | ASTM D 792 | |
| Filler Content | 10 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.6-1.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.7-1 | % | SABIC method | |
| Melt Flow Rate, 250°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 90 | g/10 min | ASTM D 1238 | |
| Density | 1.35 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/1.2 kg | 9 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 50 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 80 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 110 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.4 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.015 | - | ASTM D 150 | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.4 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 | |
| Comparative Tracking Index, M | 150 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 1.5 mm | 800 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 2.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 750 | °C | IEC 60695-2-13 | |
| Injection Molding | ||||
| Drying Temperature | 110-120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250-270 | °C | ||
| Nozzle Temperature | 240-260 | °C | ||
| Front - Zone 3 Temperature | 245-265 | °C | ||
| Middle - Zone 2 Temperature | 240-255 | °C | ||
| Rear - Zone 1 Temperature | 230-245 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 40-100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8619 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8338 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7335 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6782 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6174 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5437 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5434 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：5037 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：5000 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4990 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4810 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4742 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4698 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4642 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4526
推薦文章
PC/PET(PC+PET合金)GMB1110|三菱工程塑料|物性表參數三菱工程塑料Iupilon PC/PET GMB1110是耐化學聚碳酸酯/Polyester合金品級,體積熔融指數8.6厘米3/10分鍾; 易脫模; 注塑成型,被廣泛地用於各種工業生產，如運動器械、汽車部件、光學儀器、機械、辦公自動化設備和電子設備，獲得了客戶的廣泛信賴和支持。Iupilon PC/PET GMB1110物性表參數PDF文檔下載以下是PC/PET(PC+PE
PC(聚碳酸酯)PCM-2301/韓國樂天化學/物性表參數韓國樂天化學的LOTTE Chemical HOPELEX PC PCM-2301 是一種聚碳酸脂塑料(Polycarbonate)，光滑表麵 ，特性是加粉碎30%玻璃纖維，應用於工業製品。 以下是PC(聚碳酸酯)PCM-2301/韓國樂天化學/物性表參
PP(聚丙烯)HF409|韓華道達爾(Hanwha)物性表參數韓華道達爾(Hanwha)高抗衝PP HF409是用於流延薄膜用途的均聚聚丙烯，尤其HF409是高等規聚丙烯均聚物，具有優異的耐熱性和超高的彎曲模量.其特點是：良好的爽滑性能、高透明度。韓華道達爾PP HF409物性表參數PDF文檔下載生產商：韓華道達爾PP中文名稱：(聚丙烯)以下是PP(聚丙烯)HF409|韓華道達爾(Hanwha)物性表參數物理性能額
PC(聚碳酸酯)ECF2010R|三菱工程塑料|物性表參數三菱工程塑料Iupilon PC ECF2010R是加10%炭纖複合強化,無溴無磷阻燃級,體積熔融指數10厘米3/10分鍾; 易脫模; 注塑成型,被廣泛地用於各種工業生產，如運動器械、汽車部件、光學儀器、機械、辦公自動化設備和電子設備，獲得了客戶的廣泛信賴和支持。Iupilon PC ECF2010R物性表參數PDF文檔下載以下是PC(聚碳酸酯)ECF2010
CYCOLOY(沙伯基礎)CY6414(PC/ABS合金)物性表參數SABIC(沙伯基礎)CYCOLOY CY6414 PC/ABS是一種可以注射成型的高熱等級,這種非氯化、非溴化阻燃的衝擊改性PC具有UL V0和5VB防火等級,cycoloycy(沙伯基礎)6414樹脂是各種應用的優秀候選，包括電器、照明和電氣。
PC(聚碳酸酯)GN-3630H|TEIJIN(帝人)物性表參數TEIJIN(帝人)Panlite PC GN-3630H 是一款添加30%玻璃纖維增強材料的PC塑膠原料，特性是 低異向性 ; 剛性，高 ; 良好的抗蠕變性, 優良外觀 , 耐氣候影響性能良好, 無溴 阻燃級別, 應用於 電氣元件
LCP(工業化液晶聚合物)A470|寶理塑料|物性表參數日本寶理LAPEROS LCP A470 是一種加50%纖維,高強度,高韌性,低翹曲性, 高剛性液晶高分子,是我們從傳統的塑料所想象不到的，具有非常特別的結構和性能的高分子，取Themotropic Liquid Crystal P
PC(聚碳酸酯)ME205/萬華化學/物性表參數萬華化學Clarnate PC ME205是一種聚碳酸酯無色透明，醫療級PC，耐環氧乙烷、蒸汽消毒，高粘度，易脫模，粒料，注塑，流動溶指是20,廣泛用於外殼（手提機器、家電、電子機器）、充電池外殼、托盤（低溫倉庫）、室外安裝機器外殼等。以下是PC(聚碳酸酯)ME205/萬華化學/物性表參數產品特性易脫模醫療級環氧乙烷滅菌(EtO)耐蒸煮
PC/AK3020/PC物性表參數日本出光TARFLON PC AK3020 是一種無溴阻燃1.00mmV-0阻燃等級的PC聚碳酸酯,廣泛用於打印機和複印機零部件、液晶投影儀零部件、接線端子、繼電器外殼、連接器、模塊插頭、燈箱、LED燈、蓄
PC/ABS（PC合金）GN5101RF|LUPOY(LG化學)物性表參數LG工程塑料LUPOY PC/ABS GN5101RF詳細介紹 PC/ABS GN5101RF 廣泛使用的塑料更硬、更輕，是用作工業材料高功能性塑料工程塑料中的一種。聚碳酸脂也是防彈玻璃的材料，具有耐衝擊性、耐熱性、