VALOX(沙伯基礎)4031/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX 4031 PBT是一種加30%高強度玻璃纖維增強PBT注塑樹脂，具有優異的強度、剛度和耐熱性,用途:電器手柄、射燈、電機。
 |
沙伯基礎創新塑料的VALOX 4031 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)4031/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10000 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7900 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 210 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 125 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 125 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 65 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 60 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 880 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 880 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 55 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 11 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 12 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 12 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.1E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 3.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 1.98E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.73E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 215 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.54 | - | ASTM D 792 | |
| Filler Content | 30 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-1 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Density | 1.54 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.26 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 12 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 150 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.0016 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.84 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 6 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8529 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8238 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7163 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6687 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6094 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5386 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5356 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：4958 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4932 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：4870 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4768 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4675 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4646 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4602 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4473
推薦文章
PC(聚碳酸酯)ELV2010|三菱工程塑料|物性表參數三菱工程塑料Iupilon PC ELV2010是加5%弗素樹脂複合強化,耐磨抗刮花品級,體積熔融指數10厘米3/10分鍾; 易脫模; 注塑成型,被廣泛地用於各種工業生產，如運動器械、汽車部件、光學儀器、機械、辦公自動化設備和電子設備，獲得了客戶的廣泛信賴和支持。Iupilon PC ELV2010物性表參數PDF文檔下載以下是PC(聚碳酸酯)ELV201
POM(聚甲醛樹脂)GA510|旭化成(AsahiKASEI)物性表參數旭化成(AsahiKASEI)TENAC(鐵耐克)POM 4012是一種加10%玻璃纖維增強材料聚甲醛樹脂，密度 1.50(g/cm³)，彎曲模量3200(MPa) ，簡支梁缺口衝擊強度4.0(kJ/m²) ，典型用途領域包括工程/工業配件、房屋和汽車行業。以下是POM(聚甲醛樹脂)GA510|旭化成(AsahiKASEI)物性表參數物理性能額定值單位製測試方法比重 1.50g/cm³ASTM D
PBT(聚對苯二甲酸丁二酯)LT530FR|寶理塑料|物性表參數日本寶理DURANEX PBT LT530FR 是一種GF30%增強,特殊級,耐水解, 超耐熱衝擊性的聚酯聚合物,由於它具有高的熔點和結晶度，由於其吸水率和線性熱膨脹係數很低，因此具有優良的尺寸穩定性。
PC(聚碳酸酯)A1225/萬華化學/物性表參數萬華化學Clarnate PC A1225是一種聚碳酸酯無色透明，耐熱，抗衝擊，低粘度，流動溶指是20,廣泛用於外殼（手提機器、家電、電子機器）、充電池外殼、托盤（低溫倉庫）、室外安裝機器外殼等。以下是PC(聚碳酸酯)A1225/萬華化學/物性表參數產品特性易脫模低粘度顏色形狀粒狀透明成型方式注塑技術參數物理性能值/單位測試標準測
PPS(聚苯硫醚)1130T6|寶理塑料|物性表參數日本寶理 PPS DURAFIDE 1130T6 是一種特殊級,高耐衝擊的聚苯硫醚,其用途不僅限於電子零件。可應用於燈座、水泵、各種電裝部件等，作為汽車部件、OA設備、AV設備的功能部件的材料也可發
PFA(氟聚合物樹脂)AP-211SH/大金氟化工/物性表參數大金氟化工(NEOFLON)PFA AP-211SH是一種四氟乙烯-全氟烷氧基醚共聚物樹脂，這種氟聚合物樹脂是具有耐熱性、耐化學品性、耐候性，可進行熔融加工，熔流率(熔體流動速率)MFR(14g/10分)，它有著很寬的溫度範圍內(200℃到260℃)能夠保持機械穩定，樹脂析出物微量，流動性好，機械穩定性優異，適用於晶片花籃、接頭、泵材等注射
PP(聚丙烯)GP1007F|Lupol(LG化學)物性表參數LG化學的Lupol PP GP1007F 是一款阻燃級別的聚丙烯，熔融體積流量是11cm/10min，根據物理特性和加工方法其種類也多種多樣，是具有代表性通用塑料中的一種，抗張強度、衝擊強度等比
TPU(熱塑性聚氨酯彈性體)WHT-1495EC/萬華化學/物性表參數萬華化學Wanthane TPU WHT-1495EC是一種聚酯熱塑性聚氨酯彈性體，比重是1.21g/cm³，肖氏硬度是92A，用於注塑和擠出應用，以透明，半透明，無色或微黃色顆粒的形式提供，具有優異的強度回彈性和透明度，應用於充氣管、透明鞋底等。以下是TPU(熱塑性聚氨酯彈性體)WHT-1495EC/萬華化學/物性表參數基本信息特性良好的強度清晰度
PC(聚碳酸酯)MN-4805Z|TEIJIN(帝人)物性表參數TEIJIN(帝人)Panlite PC MN-4805Z 是一款熔融體積流量是6MVR cm/10min，特性是耐候性，脫模性能良好; 無溴; 阻燃性，應用於LEDs; 反射鏡; 照明，Panlite在耐衝擊性、耐熱性、尺寸穩定性、電學特性、
PETG(共聚聚酯)K2012/韓國SK化工/物性表參數韓國SK化工SKYGREEN PETG K2012 是高功能PETG樹脂SKYGREEN是不含有環境激素Bisphenol A的環保型材料，透明性與耐化學性優秀，快速替代PC、PMMA、PVC等原有材料，並且加工功能與成型功能卓越，從