VALOX(沙伯基礎)VX4930/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX VX4930 PBT是一種加30%玻璃增強有核PBT/ASA共混物，具有優異的機械性能、高維穩性和低密度,應用領域:連接器及汽車工業。
 |
沙伯基礎創新塑料的VALOX VX4930 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)VX4930/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2.8 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2.8 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 9500 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 175 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7700 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 65 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 130 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 130 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2.8 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2.8 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 9600 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 185 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 180 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 2.9 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8200 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 210 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 116 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 45 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 800 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 800 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 78 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 45 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 25 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 218 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 182 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.2E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.15E-04 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.26 | W/m-°C | ISO 8302 | |
| CTE, 23°C to 60°C, flow | 2.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 1.15E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 218 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 182 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 182 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 50 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 50 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.46 | - | ASTM D 792 | |
| Filler Content | 30 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.1-0.3 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.7 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.3-0.7 | % | SABIC method | |
| Melt Flow Rate, 200°C/3.8 kgf | 13 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 35 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 35 | g/10 min | ASTM D 1238 | |
| Density | 1.46 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.71 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.23 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 13 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 25 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 130 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 3.2 mm | 21 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.2 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.0024 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.0182 | - | IEC 60250 | |
| Comparative Tracking Index | 500 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.6 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.75 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8619 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8338 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7335 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6782 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6174 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5437 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5434 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：5037 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：5000 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4990 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4810 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4742 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4698 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4642 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4526
推薦文章
TPE/G2712-1000-02/TPE物性表參數美國普立萬GLS係列Dynaflex TPE G2712-1000-02 是一種容易加工的熱塑彈性體化合物,設計用於要求符合FDA標準的注射模塑和擠出成型應用, 穿刺後再封閉性能佳 , 可以重疊模塑方式粘接在聚丙烯
LEXAN(沙伯基礎)HPS4/PC(聚碳酸酯)物性表參數沙伯基礎SABIC塑料 LEXAN HPS4 聚碳酸酯（PC） 是 一種 中等流動性原料， MVR（300C / 1.2kg）為16.這是一種生物相容性（ISO10993或USP VI級），適用於醫療器械應用, 它是 EtO，蒸汽，電子束和伽瑪
塞拉尼斯TPV 121-65W233|Santoprene物性表參數Celanese(塞拉尼斯)SANTOPRENE(山都坪)TPV 121-65W233是一種熱塑性硫化彈性體，它也是一種柔軟的黑色熱塑性硫化膠(TPV)，這種材料是特製的，用於粘合硫或過氧化物固化的熱固性EPDM橡膠，用於角成型，端蓋和特殊固定應用，這種級別的山托丁烯TPV是剪切依賴的，可以在傳統的熱塑性塑料設備上進行注射成型加工，它是聚烯烴為基
TPV(熱塑性硫化橡膠)8211-35/塞拉尼斯/物性表參數塞拉尼斯Santoprene TPV 8211-35是一種硬度38A的TPV(熱塑性硫化彈性體)，比重是0.930g/cm，耐連續高溫度 (1008 hr)135C，這種材料同時具有良好的物理性質和耐化學性，適用於廣泛的領域，這一牌號的TPV是剪切速率依賴型產品，可在常規熱塑性注塑成型或擠出成型設備上加工，這是一種聚烯烴基材料，可在生產過程中進行回收利用
PPS（聚苯硫醚）R-4-02/菲利浦/物性表參數Chevron Phillips 菲利普 PPS R-4-02 物性表參數 PPS R-4-02 是美國雪佛龍菲利普工程塑料聚苯硫醚 PPS 係列 Ryton 型號之一 為您提供美國雪佛龍菲利普耐高溫工程塑料聚苯硫醚 PPS R-4-02 的中英文物
LCP(液晶高分子聚合物)270B3TL/長春化工/物性表參數長春化工的LONGLITE LCP 270B3TL 是一種加30%玻璃纖維增強液晶高分子聚合物材料，性能是尺寸安定性佳、流動性極佳、耐溶劑性、高機械強度，成型加工條件參考為：成型溫度300~390℃；模具
LEXAN(沙伯基礎)505R/PC(聚碳酸酯)物性表參數沙伯基礎SABIC塑料 LEXAN 505R 聚碳酸酯（PC）是一種可注射成型的非氯化和非溴化阻燃級，填充10％玻璃纖維, 它具有UL94 V0@1.5mm的額定值，並提供各種不透明顏色選項, 這是LEXAN 500,500R，50
POE(聚烯烴彈性體)3000/埃克森美孚(ExxonMobil)物性表參數埃克森美孚(ExxonMobil)Vistamaxx(威達美)POE 3000是一種高性能聚合物，主要由乙烯隨機分布的等聚丙烯重複單元組成，采用埃克森美孚專有的茂金屬催化劑技術生產，熔體流動速率(230°C/2.16kg)是3.6克/10分鍾，密度(23°C)是0.873克/厘米³，它具有適度的彈性，易於加工，並且與各類烴基聚合物相容，它以散粒形式供應。以下是
PC(聚碳酸酯)LED2643/科思創/物性表參數德國科思創Makrolon PC LED2643 是全球品級; 體積熔融指數10厘米3/10分鍾,應用於LED照明、光學和透鏡;PC最高傳輸;介質粘度;紫外線穩定。 德國科思創Makrolon PC LED2643物性表參數PDF文檔下載 以下
PA6(尼龍6)BG30XF30/德國朗盛/物性表參數德國朗盛 LANXESS Durethan PA6 BG30XF30 是一種加30%玻璃/玻璃球，注塑，阻燃劑，低傾向於翹曲，改善表麵光潔度尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即