VALOX(沙伯基礎)VX5022/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX VX5022 PBT是一種加20%玻璃纖維增強PBT+PC共混物，具有低翹曲性能,這個等級是5021，減少翹曲。
 |
沙伯基礎創新塑料的VALOX VX5022 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)VX5022/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7300 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7100 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 205 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 645 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 65 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 200 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 2.49E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.87E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.43E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 200 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.39 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.5 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.9 | % | SABIC method | |
| Melt Flow Rate, 250°C/2.16 kgf | 16 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Density | 1.39 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 28 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 215 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.3 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.014 | - | ASTM D 150 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+16 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+16 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.3 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Comparative Tracking Index, M | 100 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Flammability Index 850°C, passes at | 2 | mm | IEC 60695-2-12 | |
| Oxygen Index (LOI) | 23 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8614 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8330 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7312 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6773 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6169 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5432 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5429 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：5018 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：4985 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4981 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4801 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4735 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4695 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4639 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4521
推薦文章
PA46(尼龍46)WTP81|恩驊力(Envalior)物性表參數恩驊力(Envalior)(原帝斯曼DSM)Stanyl聚合物PA46 WTP81是一款加熱穩定,注塑成型的PA46原料，應用於EPS轉向組件、齒輪、撓性聯軸器和傳感器、EPS齒輪、油泵齒輪（汽車），Stanyl作為高性能聚酰胺,在對耐熱性、設計硬度、摩擦磨耗以及流動性都有要求的嚴苛的應用中表現優異，Stanyl能在高達220°C時依舊保持良好的機械性能，這
PC(聚碳酸酯)FXE4272L/沙伯基礎/物性表參數Lexan PC FXE4272L 樹脂是是20%的玻璃填充，衝擊改性聚碳酸酯具有優異的遮光性能。適用於高流量、高表麵外觀、增強釋放和良好的衝擊延展性。FXE4472L有白色，理想的光屏蔽應用。 PC FXE
PP(聚丙烯)BJ520/韓華道達爾/物性表參數韓華道達爾嵌段 PP BJ520 是適用於注塑成型用途，恰當的橡膠設計使BJ355具有優異的剛性和衝擊強度平衡性.其特點是：良好的熱封性、高剛性、高衝擊強度、易脫模。 韓華道達爾PP BJ52
PA6(尼龍6)8254HS|BASF(巴斯夫)物性表參數巴斯夫ULTRAMID PA6 8254HS 尼龍樹脂顏色是黑色102色號，巴斯夫尼龍是以聚酰胺為基礎的聚酰胺成型化合物，由於它們良好的性質 ，這些材料已經成為幾乎所有工程領域中的多種部件和
LEXAN/LUX9612G/PC物性表參數沙伯基礎SABIC塑料 LEXAN LUX9612G 聚碳酸酯（PC） 是 一種可注塑材料，具有MVR（300C / 1.2kg）7,它含有非溴化，非氯化阻燃係統，額定值為UL-94 V0@1.5mm, 這種紫外線穩定等級具有擴散效果和薄壁
PBT(聚對苯二甲酸丁二酯)SEF-515T|三菱塑料|物性表參數三菱工程塑料NOVADURAN PBT SEF-515T是一種聚對苯二甲酸丁二酯(PBT)材料，熔融體積流量（MVR)(cm³/10min)是27((250°C/5.0kg))，簡支梁缺口衝擊強度(kJ/m²)是9.0(23°C)，UL阻燃等級是V-0(0.75mm)，含有的填充物為15%玻璃纖維增強材料，加工方式為：注射成型，NOVADURAN SEF-515T主要特性為:無鹵素阻燃/額定火焰。以下
PC（聚碳酸酯）VR2020/沙伯基礎/物性表參數SABIC 沙伯基礎創新Lexan PC VR2020 物性表 提供SABIC沙伯基礎創新Lexan PC VR2020物性表及SABIC公司（原GE）的各種 工程塑料物性表 ，塑膠物性大全，囊括了所有PC塑料物性表，塑料物性大全，是
PC(聚碳酸酯)FR3710T/萬華化學/物性表參數萬華化學Clarnate PC FR3710T是一種聚碳酸酯無色透明，阻燃，抗衝擊，注塑級，流動溶指是27,廣泛用於外殼（手提機器、家電、電子機器）、充電池外殼、托盤（低溫倉庫）、室外安裝機器外殼等。以下是PC(聚碳酸酯)FR3710T/萬華化學/物性表參數產品特性阻燃易脫模高粘度顏色形狀粒狀透明成型方式注塑擠出技術參數物理性能值/單
PC(聚碳酸酯)ML7689/沙伯基礎/物性表參數LEXAN PC ML7689 聚碳酸酯(PC)樹脂是一種高粘度的注塑成型(IM)，具有良好的加工性能，與標準的PC樹脂相比，具有較短的IM周期時間。該樹脂提供極低的溫度(-40度C)延展性。LEXAN ML7689resin是
Makrolon(模克隆)2467|科思創|PC(聚碳酸酯)物性表參數科思創Makrolon 2467 PC 是全球品級; 體積熔融指數是MVR (300 C/1.2 kg) 19 cm/10 min,低粘度抗紫外線防火VO級PC塑膠原料,PC 2467主要用於各種防火器材。 Makrolon 2467 PC物性表參數PDF文檔下載 以下是科