PC(聚碳酸酯)EXL1330/沙伯基礎(SABIC)物性表參數
SABIC(沙伯基礎創新塑料)LEXAN PC EXL1330是聚碳酸酯(PC)矽氧烷共聚物樹脂，也是一種UV穩定不透明注塑(IM)和板材擠出級樹脂,與標準PC相比，這種樹脂具有低溫(-60攝氏度)的延性、介質流動特性和優異的加工性能，並可縮短IM循環時間,LEXAN EXL1330樹脂是一種通用產品，可提供廣泛的不透明顏色。
 |
PC(聚碳酸酯)EXL1330/沙伯基礎(SABIC)物性表參數PDF文檔下載 |
以下是PC(聚碳酸酯)EXL1330/沙伯基礎(SABIC)物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| FLAME CHARACTERISTICS | 1) | |||
| UL Yellow Card Link | E45329-100079881 | - | - | |
| UL Yellow Card Link 2 | E45329-540671 | - | - | |
| UL Recognized, 94HB Flame Class Rating | ≥0.8 | mm | UL 94 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 1.5 mm | 875 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 875 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 0.8 mm | 875 | °C | IEC 60695-2-13 | |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 | |
| Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 | |
| Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 | |
| Glow Wire Flammability Index, 0.8 mm | 850 | °C | IEC 60695-2-12 | |
| UV-light, water exposure/immersion | F1 | - | UL 746C | |
| Oxygen Index (LOI) | 35 | % | ISO 4589 | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 61 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 130 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 2100 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 88 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2060 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 56 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | >100 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 90 | MPa | ISO 2039-1 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 801 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 680 | J/m | ASTM D 256 | |
| Izod Impact, notched, -50°C | 587 | J/m | ASTM D 256 | |
| Izod Impact, notched, 23°C, 6.4mm | 640 | J/m | ASTM D 256 | |
| Izod Impact, double-gated, 23°C | 1068 | J/m | SABIC method | |
| Instrumented Impact Total Energy, 23°C | 52 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 75 | kJ/m² | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 143 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 134 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 124 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 6.66E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 6.66E-05 | 1/°C | ASTM E 831 | |
| CTE, 23°C to 80°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 143 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 1) | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 1) | 115 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 1) | 125 | °C | UL 746B |
| PHYSICAL | ||||
| Specific Gravity | 1.18 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.4-0.8 | % | SABIC method | |
| Mold Shrinkage, xflow, 3.2 mm | 0.4-0.8 | % | SABIC method | |
| Melt Flow Rate, 300°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 | |
| Density | 1.18 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/saturated) | 0.35 | % | ISO 62-1 | |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm³/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| Hot-Wire Ignition (HWI), PLC 0 | ≥0.8 | mm | UL 746A | |
| High Amp Arc Ignition (HAI), PLC 0 | ≥0.8 | mm | UL 746A | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 3-4 | hrs | ||
| Drying Time (Cumulative) | 48 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 295-315 | °C | ||
| Nozzle Temperature | 290-310 | °C | ||
| Front - Zone 3 Temperature | 295-315 | °C | ||
| Middle - Zone 2 Temperature | 280-305 | °C | ||
| Rear - Zone 1 Temperature | 270-295 | °C | ||
| Mold Temperature | 70-95 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 40-70 | rpm | ||
| Shot to Cylinder Size | 40-60 | % | ||
| Vent Depth | 0.025-0.076 | mm | ||
| Sheet Extrusion | ||||
| Drying Temperature | 110-120 | °C | ||
| Drying Time | 3-4 | hrs | ||
| Drying Time (Cumulative) | 48 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 245-260 | °C | ||
| Barrel - Zone 1 Temperature | 250-290 | °C | ||
| Barrel - Zone 2 Temperature | 245-270 | °C | ||
| Barrel - Zone 3 Temperature | 225-255 | °C | ||
| Adapter Temperature | 225-255 | °C | ||
| Die Temperature | 240-260 | °C | ||
| Roll Stack Temp - Top | 75-115 | °C | ||
| Roll Stack Temp - Middle | 80-125 | °C | ||
| Roll Stack Temp - Bottom | 120-145 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
為及時發現和糾正網站存在的信息內容等方麵問題，在使用網站時及時反饋網站問題，從而幫助推進網站信息內容建設工作，提高網站信息互動交流。
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8614 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8330 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7312 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6773 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6169 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5432 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5429 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：5018 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：4985 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4981 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4801 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4735 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4695 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4639 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4521
推薦文章
PP(聚丙烯)TE5107|LUPOL(LG化學)物性表參數LG化學的Lupol PP TE5107 是一款加礦物填料，橡膠抗衝改性複合聚丙烯,熔融體積流量是29cm/10min,根據物理特性和加工方法其種類也多種多樣,是具有代表性通用塑料中的一種，抗張強度、
PC(聚碳酸酯)PC-1600/韓國樂天化學/物性表參數韓國樂天化學的LOTTE Chemical HOPELEX PC PC-1600 是一種聚碳酸脂塑料(Polycarbonate)，特性是超低粘度、高純度、高強度，用於複合材料。 以下是PC(聚碳酸酯)PC-1600/韓國樂天化學/物性表參數 特性
PC(聚碳酸酯)SLX9271T/沙伯基礎(SABIC)物性表參數SABIC(沙伯基礎創新塑料)LEXAN PC SLX9271T 是一種無鹵阻燃聚碳酸酯共聚物樹脂，（熔體流動速率）(300C/1.2 kg) 18.0g/10 min，拉伸模量是2400MPa，增強了UV穩定性，並添加了釋放劑，阻燃UL-94 V0額
PPS(聚苯硫醚)Z-200-E5/日本油墨DIC/物性表參數日本油墨DIC PPS Z-200-E5 是一種非增強的超韌性PPS複合材料,與FZ-2100相比具有優異的柔性和韌性,具有熔點約280℃的高耐熱性能及優良的耐藥品性,無需添加阻燃劑即可自熄的高阻燃性的樹脂
PC（聚碳酸酯）FXD103R|沙伯基礎|物性表參數沙伯基礎PC FXD103R是一個光擴散材料，它是VisualFX家族的一部分，這些效果已被開發，以滿足日益增長的審美需求，在市場，色包可能會影響性能，建議應用測試。以下是PC（聚碳酸酯）FXD103R|沙伯基礎|物性表參數物理性能額定值 (公製)額定值 (英製)測試方法比重1.20 g/cc1.20 g/ccASTM D792密度1.20 g/cc0
PBT(聚對苯二甲酸丁二酯)756HA|寶理塑料|物性表參數日本寶理DURANEX PBT 756HA 是一種GF增強, ,低翹曲,優質外觀性, 阻燃的聚酯聚合物,由於它具有高的熔點和結晶度，由於其吸水率和線性熱膨脹係數很低，因此具有優良的尺寸穩定性。此外，
PP(聚丙烯)GP3200|LUPOL(LG化學)物性表參數LG化學的Lupol PP GP3200 是一款加20%礦物填料，通用級別的聚丙烯，熔融體積流量是10cm/10min，根據物理特性和加工方法其種類也多種多樣，是具有代表性通用塑料中的一種，抗張強度、
PA66(尼龍66)CM3003G1000|TORAY(東麗)物性表參數TORAY(東麗)Nylon樹脂AMILAN PA66 CM3003G1000 是一種未增強，耐磨損級別的尼龍66原料，拉伸強度在23℃測試條件是100MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需求和
PP(聚丙烯)Clyrell/EC340Q/利安德巴塞爾/物性表參數利安德巴塞爾(LyondellBasell)Clyrell PP EC340Q 是一種是專門設計用於注塑成型的成核聚丙烯抗衝共聚物，Clyrell EC340Q具有出色的衝擊強度/剛度組合，易於加工，低應力美白，極高的光澤度和低
ABS(丙烯腈丁二烯苯乙烯)EX75|沙伯基礎|物性表參數SABIC(沙伯基礎)CYCOLAC ABS EX75是一種多用途擠壓ABS材料,提供良好的平衡工程性能,在機械、電氣、紡織、汽車、飛機、輪船等製造工業及化工中獲得了廣泛的應用。CYCOLAC EX75 ABS物性表參數PDF文檔下載以下是ABS(丙烯腈丁二烯苯乙烯)EX75|沙伯基礎|物性表參數物理性能額定值單位製測試方法比重 1.04g/cm³ASTM D792溶化體積