日期：2020-11-03 03:14:41 編輯：科思德塑膠來源：科思德塑膠瀏覽：828

沙伯基礎(SABIC)Noryl PPO SE1X是一種PPE + PS(聚苯醚)，這種改性聚苯醚樹脂是無溴化，無氯化的FR防火，UL94 V1, UL746C F1，絕緣強度，適用於電子/電子市場室內/室外應用。。

以下是PPO(聚苯醚)SE1X/沙伯基礎(Noryl)物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E207780-100107147	-	-
UL Yellow Card Link 2		E45587-100107136	-	-
UL Recognized, 94V-0 Flame Class Rating		≥6	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating		≥1.5	mm	UL 94
Glow Wire Flammability Index, 1.0 mm		900	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm		900	°C	IEC 60695-2-12
Glow Wire Flammability Index, 2.0 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 3.0 mm		960	°C	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm		700	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm		700	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm		725	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm		725	°C	IEC 60695-2-13
Radiant Panel Listing		RP100	-	UL Tested
UV-light, water exposure/immersion		F1	-	UL 746C
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min		65	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min		53	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min		4	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min		15	%	ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span		100	MPa	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span		2400	MPa	ASTM D 790
IMPACT
Izod Impact, notched, 23°C		180	J/m	ASTM D 256
Izod Impact, notched, -30°C		106	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C		51	J	ASTM D 3763
Instrumented Impact Energy @ peak, -30		32	J	ASTM D 3763
THERMAL
HDT, 0.45 MPa, 6.4 mm, unannealed		126	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed		118	°C	ASTM D 648
Relative Temp Index, Elec	¹⁾	110	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	110	°C	UL 746B
PHYSICAL
Specific Gravity		1.1	-	ASTM D 792
Water Absorption, (23°C/24hrs)		0.06	%	ASTM D 570
Mold Shrinkage, flow, 3.2 mm		0.5-0.7	%	SABIC method
Mold Shrinkage on Tensile Bar, xflow		0.5-0.7	%	SABIC method
ELECTRICAL
Volume Resistivity		2.3E+16	Ohm-cm	ASTM D 257
Surface Resistivity		>1.E+15	Ohm	ASTM D 257
Dielectric Strength, in oil, 3.2 mm		18.1	kV/mm	ASTM D 149
Relative Permittivity, 50/60 Hz		2.52	-	ASTM D 150
Relative Permittivity, 1 MHz		2.46	-	ASTM D 150
Dissipation Factor, 50/60 Hz		0.0034	-	ASTM D 150
Dissipation Factor, 1 MHz		0.0021	-	ASTM D 150
Arc Resistance, Tungsten {PLC}		6	PLC Code	ASTM D 495
High Voltage Arc Track Rate {PLC}		4	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}		1	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 0		≥1.5	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0		≥1.5	mm	UL 746A
Injection Molding
Drying Temperature		105-110	°C
Drying Time		3-4	hrs
Drying Time (Cumulative)		8	hrs
Maximum Moisture Content		0.02	%
Melt Temperature		280-310	°C
Nozzle Temperature		280-310	°C
Front - Zone 3 Temperature		270-310	°C
Middle - Zone 2 Temperature		260-305	°C
Rear - Zone 1 Temperature		250-300	°C
Mold Temperature		75-105	°C
Back Pressure		0.3-0.7	MPa
Screw Speed		20-100	rpm
Shot to Cylinder Size		30-70	%