德國朗盛 LANXESS Durethan PA6 BC304H3.0是一種無強化，注塑成型，提高衝擊強度，熱老化穩定尼龍6樹脂,用途:適用於在擠壓成型的容器中，如農用化學品的阻擋層,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
生產商：LANXESS(德國朗盛)、品名：Durethan
PA6(尼龍6)BC304H3.0/德國朗盛/物性表參數

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 270 °C / WZ 80 °C; 500 bar	%	acc. ISO 2577	1.14
	Molding shrinkage, transverse	150x105x3; 270 °C / WZ 80 °C; 500 bar	%	acc. ISO 2577	1.45
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.38
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.46
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	1800	800
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	45	35
	Yield strain	50 mm/min	%	ISO 527-1,-2	4.5	30
	Nominal strain at break	50 mm/min	%	ISO 527-1,-2	> 50	> 50
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	N	N
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	N	N
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	85	120
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	20	20
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	70	100
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	30	17
	Flexural modulus	2 mm/min	MPa	ISO 178-A	1600	700
	Flexural strength	2 mm/min	MPa	ISO 178-A	60	30
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	7.0	9.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	55	25
	Puncture energy	23 °C	J	ISO 6603-2	55
	Puncture energy	-30 °C	J	ISO 6603-2	60
	Ball indentation hardness		N/mm²	ISO 2039-1	80	35
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	50
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	90
	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	40
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	150
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	1.5
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	1.6
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	21
	Resistance to heat (ball pressure test)		°C	IEC 60695-10-2	194
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Burning behavior US-FMVSS302	>=1.0 mm		ISO 3795	passed
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	150
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	3.3	11
	Relative permittivity	1 MHz	-	IEC 60250	3.0	3.5
	Dissipation factor	100 Hz	10-4	IEC 60250	70	1750
	Dissipation factor	1 MHz	10-4	IEC 60250	150	900
	Volume resistivity		Ohm·m	IEC 60093	1E13	1E10
	Surface resistivity		Ohm	IEC 60093	1E15	1E14
	Electric strength	1 mm	kV/mm	IEC 60243-1	35	35
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
	Comparative tracking index CTI M	Solution B	Rating	IEC 60112	600 M - 2.3
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	7.5
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	2.2
	Density		kg/m³	ISO 1183	1060
	Bulk density		kg/m³	ISO 60	600
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	270
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	260-280
	Mold temperature		°C	-	80-90