PA6(尼龍6)BG30FN05/德國朗盛/物性表參數

日期：2020-04-25 02:34:14 編輯：科思德塑膠來源：科思德塑膠瀏覽：247

德國朗盛 LANXESS Durethan PA6 BG30FN05是一種加30%玻璃，注塑，無鹵阻燃，低翹曲傾向尼龍6樹脂,用途:適用於在擠壓成型的容器中，如農用化學品的阻擋層,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
生產商：LANXESS(德國朗盛)、品名：Durethan
PA6(尼龍6)BG30FN05/德國朗盛/物性表參數

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0,8
	Molding shrinkage, transverse	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0,8
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.2
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.2
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	5400	2100
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	75	30
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.2	>20
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	40	60
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	38	25
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	<10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	30	45
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	30	20
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	5200	2000
	Flexural strength	2 mm/min	MPa	ISO 178-A	120	45
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3	7
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A		40
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	100
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	195
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.6
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.7
	Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94	0.4 mm	Class	UL 94	V-0
	Burning behavior UL 94	0.75 mm	Class	UL 94	V-0
	Burning behavior UL 94	3.0 mm	Class	UL 94	V-0
	Resistance to heat (ball pressure test)		°C	IEC 60695-10-2	201
	Glow wire test (GWFI)	0.4 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.4 mm	°C	IEC 60695-2-13	960
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	900
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	800
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	800
Electrical properties (23 °C/50 % r. h.)
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	550
	Comparative tracking index CTI	Solution A	PLC	UL 746A	0
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	1.8
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	6
	Density		kg/m³	ISO 1183	1410
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	260
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.07
	Melt temperature (Tmin - Tmax)		°C	-	240-260
	admissible residence time at Tmax		min	-	<5
	Mold temperature		°C	-	80-100