PA6(尼龍6)BKV230H3.0/德國朗盛/物性表參數

日期：2020-04-14 09:33:34 編輯：科思德塑膠來源：科思德塑膠瀏覽：189

德國朗盛 LANXESS Durethan PA6 BKV230H3.0是一種加入30%玻璃纖維，注塑，衝擊強度提高，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA6 BKV230H3.0

以下是PA6(尼龍6)BKV230H3.0/德國朗盛/物性表參數

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.2
	Molding shrinkage, transverse	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.7
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.07
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.15
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	8000	4400
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	125	75
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	4.0	8.5
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	85	100
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	95	85
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	20	40
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	15	15
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	75	95
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	85	80
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	20	35
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	15	15
	Flexural modulus	2 mm/min	MPa	ISO 178-A	7500	4100
	Flexural strength	2 mm/min	MPa	ISO 178-A	205	115
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.3	7.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	200	90
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	213
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	190
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	210
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	1.3
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	6.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.8
	Density		kg/m³	ISO 1183	1300
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	260-290
	Mold temperature		°C	-	80-100

德國朗盛LANXESS Durethan PA6 BKV230H3.0具有高抗震及抗裂性能，具體指標與材料的等級與含水量有關。彈性體改性的材料即使在低含水量及低溫下也具有良好的韌性,硬度高，尤其對於玻纖增強級別產品；拉伸模量：1,300 到 15,700 MPa (取決於含水量),良好的機械性能及阻尼吸聲效應、低摩擦力、急速運行能力好，氣體阻隔性能好（薄膜級）.

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.