PA6(尼龍6)DPAKV30HREF/德國朗盛/物性表參數

日期：2020-04-14 10:23:32 編輯：科思德塑膠來源：科思德塑膠瀏覽：191

德國朗盛 LANXESS Durethan PA66 DP2801是一種加入30%玻璃纖維，注塑，改善流動性，耐水解尼龍66樹脂，尼龍從環境中吸收潮氣的能力也不同,這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA66 DPAKV30HREF

以下是PA6(尼龍6)DPAKV30HREF/德國朗盛/物性表參數

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.37
	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.82
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.06
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.04
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	8200	5000
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	150	100
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.6	8.0
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	80	80
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	70
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	70	70
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	65	60
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	10	15
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	8100	5000
	Flexural strength	2 mm/min	MPa	ISO 178-A	240	150
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.0	6.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	225	125
	Puncture maximum force	23 °C	N	ISO 6603-2	774
	Puncture maximum force	-30 °C	N	ISO 6603-2	756
	Puncture energy	23 °C	J	ISO 6603-2	2.7
	Puncture energy	-30 °C	J	ISO 6603-2	2.5
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	263
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	240
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	250
	Burning behavior US-FMVSS302			ISO 3795	passed
Other properties (23 °C)
	Density		kg/m³	ISO 1183	1323
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	290
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.

上一頁：PA6(尼龍6)DP2801/德國朗盛/物性表參數下一頁：PC合金樹脂/PC-330KZ/鎮江奇美/物性表參數