VALOX(沙伯基礎)VX5022/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX VX5022 PBT是一種加20%玻璃纖維增強PBT+PC共混物，具有低翹曲性能,這個等級是5021，減少翹曲。
 |
沙伯基礎創新塑料的VALOX VX5022 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)VX5022/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 125 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 7300 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7100 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 205 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 55 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 645 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 80 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 65 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 7 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 200 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 2.49E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.87E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.43E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 200 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.39 | - | ASTM D 792 | |
| Filler Content | 20 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.3-0.5 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.9 | % | SABIC method | |
| Melt Flow Rate, 250°C/2.16 kgf | 16 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Density | 1.39 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 28 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 215 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.3 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.014 | - | ASTM D 150 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+16 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+16 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 31 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.3 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Comparative Tracking Index, M | 100 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Flammability Index 850°C, passes at | 2 | mm | IEC 60695-2-12 | |
| Oxygen Index (LOI) | 23 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8575 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8286 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7226 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6737 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6139 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5416 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5401 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：4996 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4958 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：4934 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4788 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4703 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4676 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4626 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4505
推薦文章
PA66(尼龍66)70G35HSL/陶氏杜邦/物性表參數陶氏杜邦PA66 70G35HSL是一種聚酰胺66，加35%玻璃纖維增強，性能是熱穩定，顏色是NC010。原材料生產商：DuPont（陶氏杜邦）以下是PA66(尼龍66)70G35HSL/陶氏杜邦/物性表參數物理性能幹燥調節後的單位製測試方法密度 1.41--g/cm³ISO 1183收縮率 ISO 294-4 垂直流動方向1.1--%ISO 294-4
PC(聚碳酸酯)4501/沙伯基礎(SABIC)物性表參數SABIC(沙伯基礎創新塑料)LEXAN PC 4501 是一種高熱聚碳酸酯共聚物，具有良好的耐熱性、加工性和衝擊強度的平衡,provides DTUL of 290F at 264 psi。 PC(聚碳酸酯)4501/沙伯基礎(SABIC)物性表參數PDF文
LEXAN(沙伯基礎)123R/PC(聚碳酸酯)物性表參數沙伯基礎SABIC塑料 LEXAN 123R PC 是一種UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 17.5 MFR, for small，用於小而複雜的零件,抗紫外線,內部帶脫模劑。 沙伯基礎SABIC塑
LCP(工業化液晶聚合物)LX70T40F|東麗(TORAY)物性表參數東麗(TORAY)SIVERAS LCP LX70T40F 是一種加40%玻璃纖維,無機填充物增強,高韌性, 低滲氣, 低發塵工業化液晶聚合物，用於電子部件、數碼家用電器的塑料, SIVERAS由於溶融流動性出色，可以製成更加超薄的成型品。可
TPV(熱塑性硫化橡膠)271-87/塞拉尼斯/物性表參數塞拉尼斯Santoprene TPV 271-87是一種硬度93A的TPV(熱塑性硫化彈性體)，比重是0.960g/cm，耐連續高溫度 (1008 hr)135C，這種熱塑性彈性體(TPE)家族中的一種堅硬的、可著色的特種熱塑性硫化膠(TPV)，它是設計用於非脂肪食品接觸應用，該等級的Santoprene TPV是剪切依賴的，可以在傳統的熱塑性塑料設備上進行注射成型，擠出，
PC（聚碳酸酯）EXL5689|沙伯基礎|物性表參數沙伯基礎Lexan PC EXL5689聚碳酸酯(PC)樹脂是一種GF增強，UV穩定，阻燃注塑共聚物共混樹脂，這種介質流樹脂具有UL94 V0 @ 1.5mm阻燃性，基於非氯，非溴FR劑，具有優良的加工性能和改進的釋放性能, Lexan EXL5689樹脂提供了很多改善的衝擊強度和延展性比傳統的GF增強PC樹脂。該產品是廣泛應用的優秀候選人，包括電氣和電子外
光擴散PC塑料如何使用製作產品呢？市場上的原料塑料類型是很多的，其中光擴散PC塑料就是大家不可忽視的，大家子在選擇塑膠原料的時候，就要根據自己的使用需要選擇。究竟哪種PC原料可滿足大家的使用需要呢？ 大
TPE(熱塑性彈性體)TF7THT/凱柏膠寶/物性表參數凱柏膠寶KRAIBURG熱塑寶K TPE TF7THT 是一款透明, 硬度69A的FC/ht係列TPE材料,用於食品接觸應用的高透明度材料解決方案,該係列特點之一是卓越的 PP包膠性能，典型應用：剃須刀、功能和設計
Makrolon(模克隆)FR7087|科思創|PC(聚碳酸酯)物性表參數科思創Makrolon FR7087 PC 是全球品級; 體積熔融指數MVR (300 C/1.2 kg) 12 cm/10 min;加阻燃劑介質粘度抗紫外線UL 94V-0/2.2 mm和5VA/的PC塑膠原料,PC FR7087主要用於電子電氣產品。 Makrolon FR7087 PC物性表參
PA66(尼龍66)E41HSB/陶氏杜邦/物性表參數陶氏杜邦PA66 E41HSB是一種高粘度尼龍66，性能是無增強，熱穩定，顏色是NC010。原材料生產商：DuPont（陶氏杜邦）以下是PA66(尼龍66)E41HSB/陶氏杜邦/物性表參數物理性能幹燥調節後的單位製測試方法密度 1.14--g/cm³ISO 1183收縮率 ISO 294-4 垂直流動方向1.3--%ISO 294-4