LEXAN(沙伯基礎)505R/PC(聚碳酸酯)物性表參數
沙伯基礎SABIC塑料 LEXAN 505R聚碳酸酯（PC）是一種可注射成型的非氯化和非溴化阻燃級，填充10％玻璃纖維,它具有UL94 V0@1.5mm的額定值，並提供各種不透明顏色選項,這是LEXAN 500,500R，500RS，500ECR的替代品。
 |
沙伯基礎SABIC塑料LEXAN 505R PC物性表參數PDF文檔下載 |
以下是LEXAN(沙伯基礎)505R/PC(聚碳酸酯)物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 63 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 48 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 12 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 3930 | MPa | ASTM D 638 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 108 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3530 | MPa | ASTM D 790 | |
| Hardness, Rockwell M | 85 | - | ASTM D 785 | |
| Hardness, Rockwell R | 124 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 11 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 60 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 3300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 95 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3400 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 115 | MPa | ISO 2039-1 | |
| IMPACT | ||||
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 107 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 61 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | 130 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m² | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 15 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Specific Heat | 1.21 | J/g-°C | ASTM C 351 | |
| Thermal Conductivity | 0.2 | W/m-°C | ASTM C177 | |
| Vicat Softening Temp, Rate B/50 | 149 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 143 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 138 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.68E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.46E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.21 | W/m-°C | ISO 8302 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 141 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 143 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 144 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Ae | |
| HDT/Ae, 1.8 MPa Annealed 120°C, 2hrs | 136 | °C | ISO 75/Ae | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Af | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Bf | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.26 | - | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.13 | % | ASTM D 570 | |
| Water Absorption, 24 hours | 0.12 | % | ASTM D 570 | |
| Water Absorption, equilibrium, 23C | 0.31 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow | 0.2-0.6 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
| Melt Flow Rate, 300°C/1.2 kgf | 7 | g/10 min | ASTM D 1238 | |
| Density | 1.25 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.31 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.13 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 7 | cm³/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 33 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.8 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 2.9 | - | IEC 60250 | |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94-5VA Flame Class Rating | 3 | mm | UL 94 | |
| UL Compliant, 94-5VB Rating | 2 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 | |
| Oxygen Index (LOI) | 37 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 290-320 | °C | ||
| Nozzle Temperature | 280-310 | °C | ||
| Front - Zone 3 Temperature | 290-320 | °C | ||
| Middle - Zone 2 Temperature | 280-310 | °C | ||
| Rear - Zone 1 Temperature | 270-300 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 80-120 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8529 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8239 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7163 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6687 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6094 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5386 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5356 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：4958 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4932 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：4870 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4768 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4675 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4646 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4602 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4473
推薦文章
PA66(尼龍66)25WSP|美國奧升德(泛達)物性表參數奧升德VYDYNE PA66 25WSP 是一種黑色耐候性注塑級尼龍6,6樹脂。這些樹脂具有高強度、剛性、良好的韌性、高熔點、良好的表麵潤滑性和耐磨性等工程性能。Vydyne25WSP保持了尼龍對許多化學
PC(聚碳酸酯)HX3022G20/Samyang(三養)物性表參數Samyang(三養)TRIREX PCHX3022G20是一種GF強化,衝擊補強聚碳酸酯，比重是1.31g/cm³，熔流率（熔體流動速率）(300°C/1.2 kg)12g/10min，有著優異的機械特性，很好的尺寸穩定性及良好的電氣特性，應用於電子電器。以下是PC(聚碳酸酯)HX3022G20/Samyang(三養)物性表參數PROPERTYUNITASTM METHODTYPICAL DATAPhysicalSp
POM(聚甲醛共聚物)MC90/塞拉尼斯(CELANESE)物性表參數塞拉尼斯(CELANESE)Celcon POM MC90是一種加礦物增強聚甲醛共聚物，密度是1.48g/cm³，具有低翹曲，改善尺寸穩定性，改善剛度，改善實際衝擊和保留其他基礎樹脂性能，具有良好的可塑性。以下是POM(聚甲醛共聚物)MC90/塞拉尼斯(CELANESE)物性表參數基本信息黃卡編號E38860-239314填料/增強材料礦物填料特性尺寸穩定性良好低
TPE(熱塑性彈性體)TF0STT/凱柏膠寶/物性表參數凱柏膠寶KRAIBURG熱塑寶K TPE TF0STT 是一款透明, 硬度73A的FC/S係列TPE材料,用於食品接觸應用的極軟材料,擁有自然色、半透明及高透明度品種可供選擇,這些材料具有幹燥的觸感，典型應用：
PC/PET(PC+PET合金)X7507|沙伯基礎|物性表參數沙伯基礎(SABIC)XYLEX PC/PET X7507是一種耐水解PC合金,顏色是自然色，特別為泳池和水療應用而設計。XYLEX X7507 PC/PET物性表參數PDF文檔下載以下是沙伯基礎創新塑料XYLEX X7507 PC/PET物性表參數物理性能額定值單位製測試方法比重 1.20g/cm³ASTM D792, ISO 1183熔流率（熔體流動速率） (265°C/2.16 kg)8.0g/10 minASTM
PC(聚碳酸酯)PC-1000L/韓國樂天化學/物性表參數韓國樂天化學的LOTTE Chemical HOPELEX PC PC-1000L 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、防紫外線，用於汽車前照燈。 以下是PC(聚碳酸酯)PC-1000L/韓國樂天化學/物性表參數
PPS(聚苯硫醚)1130A64|寶理塑料|物性表參數日本寶理 PPS DURAFIDE 1130A64 是一種GF增強,標準, 低溢的聚苯硫醚,其用途不僅限於電子零件。可應用於燈座、水泵、各種電裝部件等，作為汽車部件、OA設備、AV設備的功能部件的材料也可
PPS(聚苯硫醚)1140A66|寶理塑料|物性表參數日本寶理 PPS DURAFIDE 1140A66 是一種GF增強 ,低氯的聚苯硫醚,其用途不僅限於電子零件。可應用於燈座、水泵、各種電裝部件等，作為汽車部件、OA設備、AV設備的功能部件的材料也可發揮其
PA46/TW200F6/PA46物性表數據荷蘭DSM公司PA46 TW200F6是由丁二胺和己二酸縮聚而成的脂肪族聚酰胺，雖然有尼龍66相似的分子結構，但Stanyl PA46的每個給定長度的鏈上的酰胺組數更多，鏈結構更對稱；而高度對稱的鏈結
TPE(熱塑性彈性體)TC3TPZ/凱柏膠寶/物性表參數凱柏膠寶KRAIBURG熱塑寶K TPE TC3TPZ 是一款黑色, 硬度28A的AD/PP/AP係列TPE材料,用於需要卓越包膠性能技術應用的材料解決方案，能包膠PP,該化合物擁有自然色和黑色可供選擇，典型應用：功