PA66(尼龍66)22G5/長春化工(漳州)/物性表參數
以下是PA66(尼龍66)22G5/長春化工(漳州)/物性表參數
| 密度 | 1.35 g/cc | 0.0488 lb/in³ | |
| 1.49 g/cc | 0.0538 lb/in³ | DAM; ISO 1183 | |
| 吸水率 | 3.4 %
@Thickness 2.00 mm
|
3.4 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 水分吸收 | 0.900 %
@Thickness 2.00 mm
|
0.900 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 粘度 | 85370 cP
@Shear Rate 5000 1/s, Temperature 280 °C
|
85370 cP
@Shear Rate 5000 1/s, Temperature 536 °F
|
ISO 11403-1 -2 |
| 138900 cP
@Shear Rate 5000 1/s, Temperature 270 °C
|
138900 cP
@Shear Rate 5000 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
| 243400 cP
@Shear Rate 5000 1/s, Temperature 260 °C
|
243400 cP
@Shear Rate 5000 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
| 270750 cP
@Shear Rate 500 1/s, Temperature 280 °C
|
270750 cP
@Shear Rate 500 1/s, Temperature 536 °F
|
ISO 11403-1 -2 | |
| 441600 cP
@Shear Rate 500 1/s, Temperature 270 °C
|
441600 cP
@Shear Rate 500 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
| 774800 cP
@Shear Rate 500 1/s, Temperature 260 °C
|
774800 cP
@Shear Rate 500 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
| 粘度測試 | 140 cm³/g | 140 cm³/g | DAM; ISO 307 1157 1628 |
| 線性成型收縮率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 線性成型收縮率，橫向 | 0.010 cm/cm | 0.010 in/in | DAM; ISO 294-4 2577 |
| 機械性能 | 額定值 (公製) | 額定值 (英製) | 測試方法 |
|---|---|---|---|
| 抗張強度(斷裂) | 110 MPa | 16000 psi | 50%RH; ISO 527-1/-2 |
| 125 MPa | 18100 psi | DAM; ISO 527-1/-2 | |
| 抗張強度 | 8.79 MPa
@Strain 0.230 %, Temperature 150 °C
|
1270 psi
@Strain 0.230 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 |
| 12.0 MPa
@Strain 0.240 %, Temperature 90.0 °C
|
1740 psi
@Strain 0.240 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 15.95 MPa
@Strain 0.470 %, Temperature 150 °C
|
2313 psi
@Strain 0.470 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 22.76 MPa
@Strain 0.480 %, Temperature 90.0 °C
|
3301 psi
@Strain 0.480 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 24.06 MPa
@Strain 0.700 %, Temperature 150 °C
|
3490 psi
@Strain 0.700 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 25.92 MPa
@Strain 0.400 %, Temperature 40.0 °C
|
3759 psi
@Strain 0.400 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 31.12 MPa
@Strain 1.10 %, Temperature 150 °C
|
4514 psi
@Strain 1.10 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 34.25 MPa
@Strain 0.790 %, Temperature 90.0 °C
|
4968 psi
@Strain 0.790 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 37.13 MPa
@Strain 0.540 %, Temperature 40.0 °C
|
5385 psi
@Strain 0.540 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 41.37 MPa
@Strain 0.570 %, Temperature 23.0 °C
|
6000 psi
@Strain 0.570 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 41.5 MPa
@Strain 0.470 %, Temperature 23.0 °C
|
6020 psi
@Strain 0.470 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 42.25 MPa
@Strain 1.55 %, Temperature 150 °C
|
6128 psi
@Strain 1.55 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 44.11 MPa
@Strain 2.01 %, Temperature 150 °C
|
6398 psi
@Strain 2.01 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 44.88 MPa
@Strain 1.15 %, Temperature 90.0 °C
|
6509 psi
@Strain 1.15 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 52.61 MPa
@Strain 3.26 %, Temperature 150 °C
|
7630 psi
@Strain 3.26 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 54.28 MPa
@Strain 0.980 %, Temperature 40.0 °C
|
7873 psi
@Strain 0.980 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 55.02 MPa
@Strain 2.75 %, Temperature 150 °C
|
7980 psi
@Strain 2.75 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 57.51 MPa
@Strain 1.63 %, Temperature 90.0 °C
|
8341 psi
@Strain 1.63 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 63.12 MPa
@Strain 2.08 %, Temperature 90.0 °C
|
9155 psi
@Strain 2.08 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 63.72 MPa
@Strain 0.650 %, Temperature -20.0 °C
|
9242 psi
@Strain 0.650 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 67.98 MPa
@Strain 0.820 %, Temperature 0.000 °C
|
9860 psi
@Strain 0.820 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 71.93 MPa
@Strain 3.50 %, Temperature 90.0 °C
|
10430 psi
@Strain 3.50 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 72.3 MPa
@Strain 0.770 %, Temperature 0.000 °C
|
10500 psi
@Strain 0.770 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 73.4 MPa
@Strain 1.26 %, Temperature 40.0 °C
|
10600 psi
@Strain 1.26 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 73.91 MPa
@Strain 1.18 %, Temperature 23.0 °C
|
10720 psi
@Strain 1.18 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 74.49 MPa
@Strain 2.80 %, Temperature 90.0 °C
|
10800 psi
@Strain 2.80 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 78.89 MPa
@Strain 0.830 %, Temperature -20.0 °C
|
11440 psi
@Strain 0.830 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 79.11 MPa
@Strain 1.75 %, Temperature 40.0 °C
|
11470 psi
@Strain 1.75 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 84.04 MPa
@Strain 1.04 %, Temperature 23.0 °C
|
12190 psi
@Strain 1.04 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 94.42 MPa
@Strain 2.82 %, Temperature 40.0 °C
|
13690 psi
@Strain 2.82 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 100.33 MPa
@Strain 1.96 %, Temperature 23.0 °C
|
14552 psi
@Strain 1.96 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 100.68 MPa
@Strain 1.34 %, Temperature 0.000 °C
|
14602 psi
@Strain 1.34 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 100.92 MPa
@Strain 2.18 %, Temperature 40.0 °C
|
14637 psi
@Strain 2.18 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 101.62 MPa
@Strain 1.11 %, Temperature -20.0 °C
|
14739 psi
@Strain 1.11 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 118.66 MPa
@Strain 1.78 %, Temperature 23.0 °C
|
17210 psi
@Strain 1.78 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 120.54 MPa
@Strain 1.46 %, Temperature 0.000 °C
|
17483 psi
@Strain 1.46 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 127.28 MPa
@Strain 1.98 %, Temperature 0.000 °C
|
18460 psi
@Strain 1.98 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 134.63 MPa
@Strain 1.66 %, Temperature -20.0 °C
|
19526 psi
@Strain 1.66 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 142.85 MPa
@Strain 1.74 %, Temperature -20.0 °C
|
20719 psi
@Strain 1.74 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 157.09 MPa
@Strain 2.33 %, Temperature 0.000 °C
|
22784 psi
@Strain 2.33 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 伸長率 (斷裂) | 2.0 % | 2.0 % | DAM; ISO 527-1/-2 |
| 2.6 % | 2.6 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 7.50 GPa | 1090 ksi | 50%RH; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | DAM; ISO 527-1/-2 | |
| 3.213 GPa
@Temperature 150 °C
|
466.0 ksi
@Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 3.595 GPa
@Temperature 150 °C
|
521.4 ksi
@Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 5.515 GPa
@Temperature 60.0 °C
|
799.9 ksi
@Temperature 140 °F
|
50%RH; ISO 11403-1 -2 | |
| 5.62 GPa
@Temperature 60.0 °C
|
815 ksi
@Temperature 140 °F
|
DAM; ISO 11403-1 -2 | |
| 10.386 GPa
@Temperature -20.0 °C
|
1506.4 ksi
@Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 10.498 GPa
@Temperature -20.0 °C
|
1522.6 ksi
@Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 割線模量 | 4.16 GPa
@Strain 2.06 %, Temperature 40.0 °C
|
603 ksi
@Strain 2.06 %, Temperature 104 °F
|
 |
PA66(尼龍66)22G5/長春化工(漳州)/物性表參數 |
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8547 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8258 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7179 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6705 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6105 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5398 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5371 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：4968 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4941 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：4886 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4776 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4683 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4664 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4608 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4477
推薦文章
PA6(尼龍6)B30SFN30/德國朗盛/物性表參數德國朗盛 LANXESS Durethan PA6 B30SFN30 是一種無增強，注塑，阻燃尼龍6樹脂,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷
Makrolon(模克隆)2665(科思創)PC(聚碳酸酯)物性表參數科思創Makrolon 2665 PC材料 介紹： Makrolon 2665 PC 是全球品級; 體積熔融指數12.5 厘米 3 /10分鍾; UL 94 V-2/1.5毫米和3.0毫米; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2665物性
PP(聚丙烯)BX3500/韓國SK/物性表參數韓國SK Global Chemical Yuplene PP BX3500是一種為注射成形的而研製的抗衝擊聚丙烯，它具有很好的耐衝性和樹脂穩定性，因此已獲得了 UL認證，熔體流動速率(230°C/2.16kg)是10克/10分鍾，YUPLENE BX3500可用於瓶蓋製造。以下是PP(聚丙烯)BX3500/韓國SK/物性表參數項目質量指示單位實驗方法熔融指數10g/10minASTM D1238
PP(聚丙烯)BI320/韓華道達爾/物性表參數韓華道達爾嵌段 PP BI320 是用於注塑用途的高衝擊高剛性PP，具有優異的衝擊強度和高剛性,這一牌號在低溫條件下具有較高的落錘衝擊強度，且具有良好的UV穩定性。適用於板條箱、托盤
PC(聚碳酸酯)XHT2141/沙伯基礎(SABIC)物性表參數SABIC(沙伯基礎創新塑料)LEXAN PC XHT2141 是一種高流動、高耐熱的聚碳酸酯共聚物，它是LEXAN XHT2141是耐高溫PC塑料樹脂，它可在一係列不透明和有限的透明顏色。 PC(聚碳酸酯)XHT2141/沙伯基礎
POM(聚甲醛共聚物)TC701/可隆(KOLON)物性表參數可隆(KOLON)Kocetal POM TC701是一種加礦物增強級的聚甲醛共聚物，比重是1.44g/cm³，熔流率(熔體流動速率)(190°C/2.16kg)24g/10min，具有良好的尺寸穩定性，應用於汽車工業 製造汽車泵、汽化器部件、輸油管、動力閥、萬向節軸承、馬達齒輪、曲軸、把手、儀表板、汽車窗升降機裝置、電開關、安全帶扣等。以下是POM(聚甲
PC/ABS(PC合金)LDS3724|三菱工程塑料|物性表參數三菱工程塑料XANTAR PC/ABS LDS3724是鐳雕級別的聚碳酸酯+ABS合金材料,體積熔融指數14厘米3/10分鍾; 密度是1.23g/cm³，拉伸模量是2250MPa，維卡軟化溫度122°C, 特性是：激光標記 ;磷含量，低（到無） ;無溴阻燃性，被廣泛地用於各種工業生產，如運動器械、汽車部件、光學儀器、機械、辦公自動化設備和電子設備，獲得了客戶
PA46(尼龍46)TE200F8|恩驊力(Envalior)物性表參數恩驊力(Envalior)(原帝斯曼DSM)Stanyl聚合物PA46 TE200F8是一款加入40%玻纖增強, 熱穩定,注塑成型的PA46原料，應用於電子電氣，Stanyl作為高性能聚酰胺,在對耐熱性、設計硬度、摩擦磨耗以及流動性都有要求的嚴苛的應用中表現優異，Stanyl能在高達220°C時依舊保持良好的機械性能，這使它比PPA、PA6T、PA9T、PPS 和LCP更適合
LEXAN/955/PC物性表參數沙伯基礎SABIC塑料 LEXAN 955 聚碳酸酯（PC） 是 一種可注射成型的非氯化/溴化，未填充的阻燃級別，具有高粘度, 它的MVR為7（300C / 1.2kg），UL94 V0 @ 1.5mm，5VA，3.0mm等級，有多種不透明顏色
CYCOLOY(沙伯基礎)CY8630(PC/ABS合金)物性表參數SABIC(沙伯基礎)CYCOLOY CY8630 PC/ABS是一種具有水解穩定性的、可注射成型的改性劑，這種非氯化、非溴化阻燃PC/ABS具有UL V0和5VA/B防火等級,CYCOLOY(沙伯基礎)CY8630樹脂是一種非常適合廣泛應用的廣泛應用，包括電器、照明、電氣和附件。