PPO(聚苯醚)SE1GFN3/沙伯基礎(Noryl)物性表參數

日期：2020-11-03 03:06:55 編輯：科思德塑膠來源：科思德塑膠瀏覽：411

沙伯基礎(SABIC)Noryl PPO SE1GFN3是一種加30%玻璃纖維增強PPE + PS(聚苯醚)，這種改性聚苯醚樹脂無溴化，無氯化的FR係統，UL94 V1級別，RTI 110/105/110，絕緣強度，尺寸穩定性，適合電子/電子應用。

以下是PPO(聚苯醚)SE1GFN3/沙伯基礎(Noryl)物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E45329-236778	-	-
UL Recognized, 94-5VA Flame Class Rating		≥3	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating		≥6	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating		≥1.5	mm	UL 94
Glow Wire Flammability Index 960°C, passes at	²⁾	3.2	mm	IEC 60695-2-12
UV-light, water exposure/immersion		F2	-	UL 746C
Oxygen Index (LOI)		31	%	ISO 4589
MECHANICAL
Taber Abrasion, CS-17, 1 kg		55	mg/1000cy	SABIC method
Tensile Stress, break, 5 mm/min		105	MPa	ISO 527
Tensile Strain, break, 5 mm/min		2	%	ISO 527
Tensile Modulus, 1 mm/min		8000	MPa	ISO 527
Flexural Stress, break, 2 mm/min		130	MPa	ISO 178
Flexural Modulus, 2 mm/min		6000	MPa	ISO 178
Ball Indentation Hardness, H358/30		130	MPa	ISO 2039-1
IMPACT
Izod Impact, unnotched 80104 +23°C		25	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C		25	kJ/m²	ISO 180/1U
Charpy 23°C, Unnotch Edgew 80104 sp=62mm		30	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80104 sp=62mm		30	kJ/m²	ISO 179/1eU
THERMAL
CTE, -40°C to 40°C, flow		3.7E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow		5.5E-05	1/°C	ASTM E 831
Thermal Conductivity		0.28	W/m-°C	ISO 8302
CTE, -40°C to 40°C, flow		3.7E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow		5.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, flow		3.E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow		7.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C		PASSES	-	IEC 60695-10-2
Ball Pressure Test, approximate maximum		140	°C	IEC 60695-10-2
Vicat Softening Temp, Rate A/50		155	°C	ISO 306
Vicat Softening Temp, Rate B/50		145	°C	ISO 306
Vicat Softening Temp, Rate B/120		150	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm		140	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm		135	°C	ISO 75/Ae
Relative Temp Index, Elec	¹⁾	110	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	110	°C	UL 746B
PHYSICAL
Mold Shrinkage on Tensile Bar, flow		0.1-0.3	%	SABIC method
Density		1.29	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)		0.23	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)		0.07	%	ISO 62
Melt Volume Rate, MVR at 280°C/10.0 kg		9	cm³/10 min	ISO 1133
ELECTRICAL
Volume Resistivity		1.E+15	Ohm-cm	IEC 60093
Surface Resistivity, ROA		>1.E+15	Ohm	IEC 60093
Dielectric Strength, in oil, 0.8 mm		30	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm		25	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm		16	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz		3	-	IEC 60250
Dissipation Factor, 50/60 Hz		0.008	-	IEC 60250
Dissipation Factor, 1 MHz		0.005	-	IEC 60250
Comparative Tracking Index	²⁾	300	V	IEC 60112
Relative Permittivity, 50/60 Hz		3.1	-	IEC 60250
Comparative Tracking Index (UL) {PLC}		3	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}		4	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 3		≥6	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4		≥1.5	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0		≥1.5	mm	UL 746A
Injection Molding
Drying Temperature		110-120	°C
Drying Time		2-3	hrs
Melt Temperature		300-320	°C
Nozzle Temperature		280-300	°C
Front - Zone 3 Temperature		300-320	°C
Middle - Zone 2 Temperature		280-300	°C
Rear - Zone 1 Temperature		260-280	°C
Hopper Temperature		80-100	°C
Mold Temperature		100-130	°C