PPO(聚苯醚)|NORYL|PX1630/沙伯基礎/物性表參數

日期：2020-11-06 02:56:48 編輯：科思德塑膠來源：科思德塑膠瀏覽：501

沙伯基礎(SABIC)NORYL PPO PX1630是一種聚苯醚(PPO) +聚苯乙烯(PS)樹脂是一種30%玻璃增強、注射成型等級提高水解穩定性的樹脂,這個等級是為水資源管理應用而開發的，NORYL PX1630已經通過認證，適用於歐洲和北美的飲用水，顏色有限。

以下是PPO(聚苯醚)PX1630/沙伯基礎(NORYL)物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
Injection Molding	¹⁾
Drying Temperature		100-120	°C
Drying Time		2-4	hrs
Maximum Moisture Content		0.02	%
Melt Temperature		280-300	°C
Nozzle Temperature		280-300	°C
Front - Zone 3 Temperature		290-310	°C
Middle - Zone 2 Temperature		270-290	°C
Rear - Zone 1 Temperature		250-270	°C
Hopper Temperature		60-80	°C
Mold Temperature		80-120	°C
FLAME CHARACTERISTICS	^{2) 3)}
UL Yellow Card Link		E45329-103460844	-	-
UL Recognized, 94HB Flame Class Rating		≥1.5	mm	UL 94
Oxygen Index (LOI)		26	%	ISO 4589
Glow Wire Flammability Index 750°C, passes at		3	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 3.0 mm		750	°C	IEC 60695-2-13
IMPACT	⁴⁾
Multiaxial Impact		6	J	ISO 6603
Izod Impact, unnotched 80104 +23°C		34	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C		30	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C		11	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C		10	kJ/m²	ISO 180/1A
MECHANICAL
Tensile Stress, break, 5 mm/min		106	MPa	ISO 527
Tensile Strain, break, 5 mm/min		2	%	ISO 527
Tensile Modulus, 1 mm/min		8100	MPa	ISO 527
Flexural Stress, break, 2 mm/min		170	MPa	ISO 178
Flexural Modulus, 2 mm/min		7050	MPa	ISO 178
Taber Abrasion, CS-17, 1 kg		70	mg/1000cy	SABIC method
Ball Indentation Hardness, H358/30		130	MPa	ISO 2039-1
THERMAL
CTE, -40°C to 40°C, flow		2.E-5	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow		7.E-5	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C		PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/50		155	°C	ISO 306
Vicat Softening Temp, Rate B/50		149	°C	ISO 306
Vicat Softening Temp, Rate B/120		158	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm		145	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm		140	°C	ISO 75/Ae
Relative Temp Index, Elec	²⁾	65	°C	UL 746B
Relative Temp Index, Mech w/impact	²⁾	65	°C	UL 746B
Relative Temp Index, Mech w/o impact	²⁾	65	°C	UL 746B
PHYSICAL
Specific Gravity		1.29	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm		0.1-0.3	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm		0.2-0.5	%	SABIC method
Water Absorption, (23°C/saturated)		0.2	%	ISO 62-1
Density		1.3	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)		0.06	%	ISO 62
Melt Volume Rate, MVR at 300°C/10.0 kg		16	cm³/10 min	ISO 1133
ELECTRICAL
Volume Resistivity		1.E+15	Ohm-cm	IEC 60093
Surface Resistivity, ROA		>1.E+15	Ohm	IEC 60093
Dielectric Strength, in oil, 3.2 mm		18	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz		2.9	-	IEC 60250
Dissipation Factor, 50/60 Hz		0.0006	-	IEC 60250
Dissipation Factor, 1 MHz		0.001	-	IEC 60250
Relative Permittivity, 50/60 Hz		2.9	-	IEC 60250