SABIC(沙伯基礎)LNP/THERMOCOMP/Compound/ PPA UX06032是一種基於聚酞酰胺樹脂的化合物，含有玻璃纖維，阻燃劑，該材料的附加特性包括:阻燃，無溴無氯阻燃，熱穩定。

以下是SABIC(沙伯基礎)LNP/THERMOCOMP/Compound/PPA/UX06032物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E45329-101284058	-	-
UL Yellow Card Link 2		E207780-103093686	-	-
UL Recognized, 94V-0 Flame Class Rating		≥0.41	mm	UL 94
Glow Wire Ignitability Temperature, 0.8 mm		825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.6 mm		825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm		850	°C	IEC 60695-2-13
Glow Wire Flammability Index, 3.0 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 0.8 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.6 mm		960	°C	IEC 60695-2-12
MECHANICAL
Tensile Stress, break, 5 mm/min		130	MPa	ISO 527
Tensile Strain, break, 5 mm/min		2.1	%	ISO 527
Tensile Modulus, 1 mm/min		11400	MPa	ISO 527
Flexural Stress, break, 2 mm/min		200	MPa	ISO 178
Flexural Modulus, 2 mm/min		9900	MPa	ISO 178
IMPACT
Izod Impact, unnotched 80104 +23°C		40	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C		5	kJ/m²	ISO 180/1A
THERMAL
CTE, 23°C to 60°C, flow		2.1E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow		5.4E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm		275	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm		258	°C	ISO 75/Af
Relative Temp Index, Elec	¹⁾	140	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	140	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	140	°C	UL 746B
PHYSICAL
Mold Shrinkage on Tensile Bar, flow		0.2-0.3	%	SABIC method
Density		1.46	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)		0.23	%	ISO 62-1
ELECTRICAL
Comparative Tracking Index	²⁾	600	V	IEC 60112
Comparative Tracking Index (UL) {PLC}		0	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 0		≥0.41	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 0		≥0.41	mm	UL 746A
Injection Molding
Drying Temperature		120-140	°C
Drying Time		4-6	hrs
Melt Temperature		305-315	°C
Front - Zone 3 Temperature		295-315	°C
Middle - Zone 2 Temperature		290-310	°C
Rear - Zone 1 Temperature		280-300	°C
Mold Temperature		130-150	°C
Back Pressure		0.2-0.3	MPa
Screw Speed		40-80	rpm